What are the processing points of PBT engineering plastics
Monotonic treatment: this kind of data is easy to hydrolyze under high temperature, so monotonic treatment before processing is very important. It is suggested that the monotonic condition in air is 120 ℃, 6-8 hours, maybe 150 ℃, 2-4 hours. It is necessary that the humidity be less than 0.03%. If the hygroscopic monotone is used, the recommended condition is 150 ℃ for 2.5 hours.
2. Melting temperature: 225-275 ℃, recommended temperature: 250 ℃.
Mold temperature: 40-60 ℃ for unreinforced type. The cooling cavity of the mold should be well designed to reduce the twists and turns of the plastic parts. The loss of heat must be fast and uniform. It is recommended that the diameter of the mold cooling cavity is 12mm.
3 injection pressure: medium (up to 1500bar).
4 injection speed: the injection speed should be as fast as possible (because PBT coagulates quickly).
5 runner and gate: Circular runner is recommended to increase pressure transmission (empirical formula: runner diameter = plastic thickness +1.5mm). Be able to use various types of gates. Warm runner can also be used, but attention should be paid to avoid data leakage and degradation. The gate diameter should be between 0.8-1.0*t, where t is the thickness of the plastic part. For submerged gates, a minimum diameter of 0.75mm is recommended.
Article source: PBT engineering plastics http://www.wcyxs8888.com/
-
04-13
PVC Engineering Plastics: how PVC plastic pipes are formed
The forming process of PVC plastic pipes should start from the raw materials of PVC plastic granules, which can be divided into soft PVC and hard PVC according to the added amount of stabilizer, plast
-
11-12
What is the filling property of Jiangmen engineering plastics
What is the filling property of Jiangmen engineering plasticsIn recent years, PC modified plastics have developed rapidly in China, and its industrial system is gradually established and improved. Th
-
10-08
Jiangmen Engineering Plastics: how to classify Jiangmen engineering plastics?
How to classify Jiangmen engineering plastics? 1. Classification by application characteristicsAccording to the different application characteristics of famous plastics, plastics are usually divided
-
08-30
Application scope of PBT engineering plastics
PBT engineering plastics are widely used in electronics, car industry, office machinery and other fields. In Japan and the developed countries in Europe, PBT engineering plastics are mainly used in t